Pre-clinical assay of the tissue integration and mechanical adhesion of several types of cyanoacrylate adhesives in the fixation of lightweight polypropylene meshes for abdominal hernia repair.

Abstract

INTRODUCTION:Lightweight (LW) polypropylene (PP) meshes better adapt to host tissue, causing less fibrosis and inflammatory responses than high-density meshes. Mesh fixation using tissue adhesives (TA) that replace conventional sutures may improve the process of hernia repair and tissue trauma. This preclinical study compares the behavior of different cyanoacrylate-based adhesives in the fixation of LW-PP meshes for hernia repair. METHODS:Partial abdominal wall defects were repaired using LW-PP Optilene meshes in New Zealand rabbits. The following groups were established according to the mesh fixation method: Suture (control), Glubran 2 (n-butyl), Ifabond (n-hexyl), SafetySeal (n-butyl) and Evobond (n-octyl). At 14, 90 and 180 days after surgery, the recovered implants were examined to assess the host tissue integration, the macrophage response and the biomechanical strength. RESULTS:All the groups showed optimal host tissue incorporation regardless of the fixation procedure. Significantly increased levels of collagen 1 and collagen 3 gene expression (p<0.001) were observed at 14 days compared to the medium- and long-term durations, where the Suture and Glubran groups showed the highest expression of collagen 1. All the adhesives increased the macrophage reaction (p<0.001) compared to sutures at all implant times. Maximal macrophage response was observed in the short-term Glubran group (p<0.01) compared to the rest of the groups. Although SafetySeal and Evobond did not reach the biomechanical resistance of sutures at 14 days, all the adhesives did reach this level in the medium- to long-term periods, providing significantly higher resistance (p<0.05). CONCLUSIONS:All the cyanoacrylates, despite inducing a significantly increased macrophage response versus sutures, showed optimal host tissue integration and long-term mechanical behavior; thus, they might be good choices for LW-PP mesh hernia repairs.