Effect of Boron Addition on the Oxide Scales Formed on 254SMO Super Austenitic Stainless Steels in High-Temperature Air

Abstract

Focusing on the serious volatilization of MoO3 in super austenitic stainless steel with a high Mo content, the influence of B on the formation of oxide film and the distribution of Cr and Mo was investigated at 900 °C and 1000 °C. Without the addition of B, Mo tends to diffuse to the surface, forming porous Cr/Mo-rich oxides, causing the volatilization of Mo. The addition of B can inhibit the diffusion of Mo to the surface, facilitate the diffusion of Cr to the surface and combines with O, providing conditions for the nucleation of Cr2O3. A large amount of Cr2O3 accumulated on the surface to form a dense passive film, which inhibited the diffusion of Mo to the surface, reduced the loss of Mo, and formed Mo/Cr-rich precipitates at grain boundaries that are close to the surface. However, it was difficult to form Mo-rich precipitates at the grain boundaries of a sample without B, which aggravated the volatilization of Mo from grain boundary to surface. Therefore, the addition of B can improve the oxidation resistance of 254SMO and inhibit the volatilization of Mo.

Keywords

• super austenitic stainless steel
• oxidation behavior
• boron
• first principle
• surface