Mechanical Reinforcement of Polyamide 6 by Cold Hydrostatic Extrusion

Abstract

This paper presents the effect of severe plastic deformation obtained using the cold hydrostatic extrusion (HE) method on the mechanical and structural properties of polyamide 6 (PA6). As a result of the plastic strain, a significant increase in ultimate tensile strength and tensile modulus were observed. Tensile strength rose by almost 500%, up to the level of 508 MPa, whereas the tensile modulus rose by about 65%. Flexural modulus increase was also observed to 3230 MPa, i.e., by approx. 160%. As a result of high plastic deformation, the structure of the polyamide 6 changed significantly, as evidenced by its fibrous nature as presented in the results of the scanning electron microscopy inspection (SEM). The surface quality of products investigated was tested using profilometry.

Keywords

• cold hydrostatic extrusion
• polyamide 6
• mechanical properties
• structure