Super Broadband at Telecom Wavelengths From RE3+-Doped SiO2-Ta2O5 Glass Ceramics Planar Waveguides

  • Karmel De Oliveira Lima,
  • Fábio José Caixeta,
  • Vítor Dos Santos De Souza,
  • Leonardo Sousa Rosa,
  • Victor Del Vecchio Soares,
  • Carolina Assunção Crumo,
  • Ivana Aparecida Borin,
  • Jefferson Luis Ferrari,
  • Rogéria Rocha Gonçalves

DOI
https://doi.org/10.3389/fchem.2022.915335
Journal volume & issue
Vol. 10

Abstract

Read online

This paper reports on the preparation of Er3+/Yb3+/Tm3+, Er3+/Yb3+/Nd3+, and Er3+/Tm3+/Nd3+ triply doped and Er3+-doped SiO2-Ta2O5 glass ceramic nanocomposites and active planar waveguides by the sol–gel process using the dip-coating technique as deposition method. The investigation of their structural, morphological, and luminescent properties using XRD, AFM, and photoluminescence analysis, are reported here. The XRD results showed the presence of L-Ta2O5 nanocrystals dispersed in the SiO2-based amorphous host for all the nanocomposites and films. The rare earth ion (RE3+) doping concentration affected both the crystallinity, and the crystallite sizes of the Ta2O5 dispersed into SiO2-Ta2O5 nanocomposites and waveguides. AFM characterization revealed crack free and smooth surface roughness and differences in viscoelasticity on the Er3+-doped SiO2-Ta2O5 films surface, which allows the identification of Ta2O5 nanocrystals on the SiO2 amorphous host. The Er3+ doped and triply doped SiO2-Ta2O5 nanocomposites displayed broad- and super broadband NIR emissions with a FWHM up to 173 nm achieved in the telecom wavelengths. The lifetime of the 4I13/2 emitting level of the Er3+-doped SiO2-Ta2O5 waveguides is strongly dependent on Er3+ concentration and an emission quenching was negligible up to 0.81 mol%. The structural and luminescent investigations indicated that RE3+-doped SiO2-Ta2O5 glass ceramics are promising candidates for photonic applications in optical devices operating in wide wavelengths at the telecom bands.

Keywords