Influence of carbon on microstructure and mechanical properties of magnetron sputtered TaW coatings

Abstract

(Ta,W) and (Ta,W):C films with ~5 at.% C were deposited by non-reactive magnetron sputtering. They crystallised in a bcc structure with a columnar microstructure. The solid solubility of C in (Ta,W) alloys is very low, which suggests that the (Ta,W):C films are supersaturated with respect to carbon. This was confirmed by diffraction and atom probe tomography (APT) showing that carbon is in the as-deposited (Ta,W):C films homogeneously distributed in the structure without carbide formation or carbon segregation. Annealing at 900 °C for 2 h showed no significant column coarsening but an increased defect density at the column boundaries in the (Ta,W):C films. The films were still supersaturated with respect to carbon but APT showed a partial segregation of carbon presumably to defect-rich column boundaries after annealing. The (Ta,W) films exhibited a hardness of ~12–13 GPa. Alloying with carbon increased the hardness to ~17 GPa. The hardness increased to ~19 GPa for the annealed (Ta,W):C films. This annealing-induced hardness increase was explained by C segregation to the more defect-rich column boundaries, which restricts dislocation movements. (Ta,W):C coatings may be a potential alternative to ceramic coatings, worth exploring further by small scale mechanical testing to investigate if these materials are ductile.

Keywords

• Nanocrystalline refractory metals
• Tantalum tungsten alloy
• Carbon supersaturation
• Magnetron sputtering