Photoluminescence Study of Undoped and Eu-Doped Alkali-Niobate Aluminosilicate Glasses and Glass-Ceramics
Abstract
In this study, the photoluminescence (PL) behavior of two aluminosilicate glass series containing alkali-niobates ranging from 0.4 to 20 mol% was investigated. The glasses exhibit an intense visible emission centered at ~18,400 cm−1 for the peralkaline series and at higher energies (~19,300 cm−1) for the metaluminous glasses. However, the photoluminescence emission intensity varies significantly with the niobate content and the bulk chemistry. PL and fluorescence lifetime measurements indicate that the broad emission bands result from the overlap of different niobate populations, whose distribution changes with niobate content. The distinct PL behavior in the two glass series was related to the structural evolution of the niobate units upon niobium addition. An enhancement of the visible emission was observed for a higher fraction of distorted [NbO6] units. Eu-doping was carried out as a structural probe of the glass network, and also to determine if these glasses could be used as potential rare earth element (REE) activators. The crystal field strength around Eu ions is strongly dependent on the bulk chemistry and the niobate content. Furthermore, the peralkaline series showed energy transfer from the host [NbO6] to Eu3+, confirming the feasibility of exploring niobate glasses and glass-ceramics as lanthanide ion-activated luminescent materials. In addition, glass-ceramics (GCs) containing alkali-niobate phases with a perovskite-like structure were developed and studied to verify the optical performance of these materials. It was verified that the bulk chemistry influences crystallization behavior, and also the photoluminescence response. The transparent GC from the metaluminous series exhibits a quenching of the Eu3+ emission, whereas an enhanced emission intensity is observed for the peralkaline GC. The latter shows a strong excitation-dependent PL emission, suggesting energy transfer and migration of electronic excitation from one Eu population to another. Additionally, Eu3+ emissions arising from the D15 and D25 excited states were observed, highlighting the low phonon energy achievable in niobo-aluminosilicate hosts.
Keywords