Study on Manufacturing Technology of Ultra-Thin/Narrow Bonding Cu Strip for Electronic Packaging

Abstract

The performance of rolling parameters and annealing processes on the microstructure and properties of Cu strip were studied by High Precision Rolling Mill, FIB, SEM, Strength Tester, and Resistivity Tester. The results show that with the increase of the reduction rate, coarse grains in the bonding Cu strip are gradually broken and refined, and the grains are flattened when the reduction rate is 80%. The tensile strength increased from 248.0 MPa to 425.5 MPa, while the elongation decreased from 8.50% to 0.91%. The growth of lattice defects and grain boundary density results in an approximately linear increase in resistivity. With the increase of annealing temperature to 400 °C, the Cu strip recovers, and the strength decreased from 456.66 MPa to 220.36 MPa while the elongation rose from 1.09% to 24.73%. The tensile strength and elongation decreased to 192.2 MPa and 20.68%, respectively, when the annealing temperature was 550 °C. The trend of yield strength of the Cu strip was basically the same as that of tensile strength. The resistivity of the Cu strip decreased rapidly during a 200~300 °C annealing temperature, then the trend slowed, and the minimum resistivity was 3.60 × 10−8 Ω·m. The optimum tension range annealing was 6–8 g; less or more than that will affect the quality of the Cu strip.

Keywords

• rolling
• annealing
• bonding Cu strip
• tensile strength
• elongation
• resistivity