Preparation of Hierarchically Porous Graphitic Carbon Spheres and Their Applications in Supercapacitors and Dye Adsorption

Abstract

Hierarchical micro-/mesoporous graphitic carbon spheres (HGCS) with a uniform diameter of ~0.35 μm were synthesized by Fe-catalyzed graphitization of amorphous carbon spheres resultant from hydrothermal carbonization. The HGCS resultant from 3 h at 900 °C with 1.0 wt % Fe catalyst had a high graphitization degree and surface area as high as 564 m2/g. They also exhibited high specific capacitance of 140 F/g at 0.2 A/g and good electrochemical stability with 94% capacitance retention after consecutive 2500 cycles. The graphitization degree of the HGCS contributed to 60% of their specific capacitance, and their specific capacitance per unit surface area was as high as 0.2 F/m2, which was much higher than in the most cases of porous amorphous carbon materials reported before. In addition, the HGCS showed a high adsorption capacity of 182.8 mg/g for methylene blue (MB), which was 12 times as high as that in the case of carbon spheres before graphitization.

Keywords

• graphitic carbon spheres
• catalytic graphitization
• hierarchical pores
• supercapacitors
• dye adsorption