Effect of Hot-Pressing Process on Mechanical Properties of UHMWPE Fiber Non-Woven Fabrics

Abstract

In order to investigate the influence of a hot-pressing process on the mechanical properties of ultra-high molecular weight polyethylene (UHMWPE) fiber non-woven fabrics with stretch and in-plane shear, UHMWPE non-woven fabric samples were prepared by adjusting the temperature, time, and pressure of the hot-pressing process, and mechanical property tests were carried out so as to clarify the influence of the hot-pressing process on the mechanical properties of the samples. The results show that the hot-pressing process mainly affects the silk–glue bonding strength of the samples; in the test range, with the increase in hot-pressing temperature and time, the tensile strength and in-plane shear strength of the samples increase and then decrease, and the best mechanical properties are obtained at 130 °C and 7 min of hot pressing, respectively; at 130 °C, the in-plane shear strength is 39.94 MPa and the tensile strength is 595.43 MPa; at 7 min, the in-plane shear strength is 63.0 MPa and the tensile strength is 643.30 MPa; with the increase in the hot-pressing pressure, the in-plane shear strength of the samples increases and then decreases, and the highest is 52.60 MPa, achieved at 8 MPa; in the range of 5–8 MPa, the tensile strength of the specimens did not change significantly, and increased significantly at 9 MPa, reaching a maximum strength of 674.55 MPa.

Keywords

• UHMWPE fiber
• non-woven fabric
• hot-pressing process
• mechanical properties