Devices under semi-on-state stress often suffer from more severe current collapse than when they are in the off-state, which causes an increase in dynamic on-resistance. Therefore, characterization of the trap states is necessary. In this study, temperature-dependent transient recovery current analysis determined a trap energy level of 0.08 eV under semi-on-state stress, implying that interface traps are responsible for current collapse. Multi-frequency capacitance–voltage (C-V) testing was performed on the MIS diode, calculating that interface trap density is in the range of 1.37×1013 to 6.07×1012cm−2eV−1 from EC−ET=0.29 eV to 0.45 eV.