Boletín de la Sociedad Española de Cerámica y Vidrio (Apr 2007)
Caracterización de espumas de pizarra con adiciones de clínquer de cemento
Abstract
The decomposition of constituents of slates under non-oxidizing atmosphere leads to the manufacturing of foams. Thus die pressing at 80MPa of slates powders (particle size <80 microns) mixed with a solid agglomerate, allows a green density close to 1,8 g/cm3 . The heating of compacts under N2-5%H2 atmosphere allows to reach a final density of 2,2 g/cm3 at 1050ºC, meanwhile at 1150ºC the compact foaming leads to densities lower than 0,4 g/cm3. Clínquer addition (5% and 10%) modifies the foam density and pore size at 1150ºC. It is necessary to increase the sintering temperature up to 1175ºC to achieve densities close to 0,4 g/cm3 when a 10% of Clínquer is added. The foams with Clínquer shows a high pore size and a compression strength within the range of glass foams: 0.4-1.5MPa.<br><br>La descomposición de los componentes de la Pizarra durante su calentamiento en condiciones no oxidantes conduce a la obtención de espumas. Así, mediante la compactación en matriz a 80MPa de polvos de Pizarra de menos de 80 μm de tamaño de partícula y con adición de un aglomerante, se obtiene una densidad en verde próxima a 1,8 g/cm3. El calentamiento de estos compactos en atmósfera de N2-5% H2 permite alcanzar densidades de 2,2 g/cm3 a 1100ºC , mientras que a 1150ºC la espumación del compacto conduce a densidades inferiores a 0,4 g/cm3. La adición de Clínquer de cemento Portland (5% y 10% en peso) modifica la densidad de la espuma a 1150ºC , teniendo que elevarse la temperatura de sinterización a 1175 ºC para alcanzarse espumas con densidades próximas a 0,4 g/cm3 con un 10% de Clínquer. Estas espumas con Clínquer presentan un elevado tamaño de poro, así como una resistencia a compresión en el intervalo de resistencias de los vidrios espumados: 0,4-1,5MPa.