Effect of reaction time on formation of silica core/shell particles

Abstract

The silica core/shell nanostructures were prepared by a wet-chemical process. Silica core particles were prepared by hydrolysis and condensation of tetraethylorthosilicate. The obtained particles (average size ∼0.4 µm) were used as templates for assembling of silica nanoparticles generated from highly basic sodium silicate solution. The silica core particles were functionalized with 3-aminopropyltriethoxysilane (APTES) to allow electrostatic assembling of silica nanoparticles on the surface of silica core particles. In order to find the optimal conditions for synthesis of silica core/shell particles with mesoporous shells, the effect of reaction time on formation of silica nanoparticles was investigated. The effect of process parameters on generation and aggregation of silica nanoparticles prepared from highly basic sodium silicate solution was also investigated. It was shown that the size of silica nanoparticles and tendency towards aggregation increase with increasing the reaction time and temperature. These behaviours were reflected on the formation of mesoporous silica shell around silica core particles. Thin and uniform mesoporous silica layers were obtained if reaction times were kept short. When the reaction time was prolonged, the thicker and non-uniform shells were obtained.

Keywords

• core/shell particles
• silica
• assembling
• mesoporous
• reaction time