Remarkable Temperature Sensitivity of Partially Carbonized Carbon Fibers with Different Microstructures and Compositions

Abstract

In order to explore effect of structure on the temperature sensitivity of partially carbonized carbon fibers, different heat treatment temperatures (700, 750 and 800 °C) and heat treatment times (3 and 9 min) were used to prepare fibers with different structures. The electrical resistivities were monitored whilst the room temperature was increased from 30 to 100 °C, which was used to characterize the temperature sensitivity. The fibers showed negative temperature coefficients in the temperature range. Infrared spectra, an element analysis, a scanning electron microscope (SEM), Raman spectroscopy and X-ray diffraction measurements were used to study the microstructure of the fibers. Through the analysis, the proportions of the graphite-like structure, graphitization degree and size of the graphite-like structure crystallite influenced the temperature sensitivity. The main electron transfer method used for the fibers was variable-range hopping. This indicated that the fibers had a potential application of preparing thermistors in polymer composites.

Keywords

• carbon fibers
• temperature sensitivity
• graphitized-like structure
• conductive mechanism