Combined Effects from Dual Incorporation of ATBC as Plasticizer and Mesoporous MCM-41 as Nucleating Agent on the PLA Isothermal Crystallization in Environmentally-Friendly Ternary Composite Systems

Abstract

Different materials, based on an L-rich polylactide (PLA) as matrix, acetyl tri-n-butyl citrate (ATBC) as plasticizer, and mesoporous Mobile Crystalline Material.41 (MCM-41) particles as nucleating agent, were attained by melt extrusion. These materials are constituted by (a) binary blends of PLA and ATBC with different contents of the latest; (b) a dual compound of PLA and a given amount of MCM-41 silica (5 wt.%); and (c) ternary composites that include PLA, ATBC at several compositions and mesoporous MCM-41 at 5 wt.%. Influence of the incorporation of the plasticizer and nucleating particles has been comprehensively analyzed on the different phase transitions: glass transition, cold crystallization, melt crystallization and melting processes. Presence of both additives moves down the temperature at which PLA phase transitions take place, while allowing the PLA crystallization from the melt at 10 °C/min in the composites. This tridimensional ordering is not noticeable in the pristine PLA matrix and, accordingly, PLA crystallization rate is considerably increased under dynamic conditions and also after isothermal crystallization from either the melt or the glassy state. An important synergistic effect of dual action of ATBC and MCM-41 has been, therefore, found.

Keywords

• PLA
• ATBC
• MCM-41
• plasticizer
• nucleating agent
• crystallization rate