Study on the Effect of Different Factors on the Change of the Phosphorus-Rich Phase in High Phosphorus Steel Slag

Abstract

With the use of high phosphorus iron ore, there is a large amount of high phosphorus steel slag formed, which is difficult to handle. How to separate the elemental phosphorus has become a key issue in the secondary utilization of steel slag. Experiments found that there were distinct phosphorus-rich phases, iron-rich phases and matrix phases in the high-phosphorus steel slag cooled with the furnace. In this study, the effects of heat treatment conditions and slag basicity on the P2O5 content, as well as the size of the phosphorus-rich phase were investigated. Taking all factors into consideration, the optimal experimental conditions were determined as the holding temperature and time of 1350 °C and 60 min, respectively, and the slag basicity of 1.8. At this time, the P2O5 content in the phosphorus-rich phase reached 24.2%, and the average size of the phosphorus-rich phase was 63.51 μm. The phosphorus-rich phase is separated by crushing and magnetic separation for making phosphate fertilizer, and the residual steel slag is used again for steelmaking, which enables the realization of the resource utilization of high phosphorus steel slag.

Keywords

• high phosphorus steel slag
• phosphorus-rich phase
• holding temperature
• binary basicity
• holding time