Inorganic lead-halide perovskite, cesium lead bromide (CsPbBr3), shows outstanding optoelectronic properties. Both solution- and melt-based methods have been proposed for CsPbBr3 crystal growth. The solution-based growth was done at low-temperature, whereas the melt-based growth was done at high-temperature. However, the comparison of optical, physical, and defect states using these two different growth conditions has been scarcely studied. Here, we have compared the thermal and optical properties of solution-grown and melt-grown single crystals of CsPbBr3. Positron Annihilation Lifetime Spectroscopy (PALS) analysis showed that melt-grown crystal has a relatively smaller number of defects than the chemical synthesis method. In addition, crystals grown using the chemical method showed a higher fluorescence lifetime than melt-grown CsPbBr3.