Effect of concurrent accumulative roll bonding (ARB) process and various heat treatment on the microstructure, texture and mechanical properties of AA1050 sheets

Abstract

This study investigated the microstructure, texture, and mechanical properties of 1050 aluminum alloy sheets that underwent the accumulative roll bonding (ARB) method. The ARB proceeded up to eight passes in three ways: conventional process, preheat between rolling passes (preheating) or anneal between rolling passes (annealing). Heat treatment was done between the ARB passes for 5 min at 150 °C. The mean grain width of the 1050 Al sheet that was 11 μm before ARB, decreased to 295.73 nm, 317.33 nm, or 339.23 nm after six ARB passes in the conventional process, annealed or preheated conditions, respectively. Concurrent heat treatments cause a decrease in the strength of the texture components of Al sheets that were elaborated by the ARB method. Even though conventional and annealed processes successfully enhanced the microhardness by ∼80% and tripled the tensile strength, these improvements were weaker in the preheated condition than the other conditions due to dynamic recovery.

Keywords

• Accumulative roll bonding (ARB)
• Heat treatment
• Aluminum
• Ultrafine-grained (UFG)
• Electron backscatter diffraction (EBSD)