Cast Microstructure and Crystallographic Features of Al₃Sc Dendrites in High Sc-Contained Al-Sc Alloys

Abstract

Al-Sc alloys containing high Sc content are employed as sputtering targets for the fabrication of high-performance piezoelectric films during magnetic sputtering. Due to the high proportion of the Al3Sc phase, their workability is quite limited, and they are often used in the as-cast state. In this study, the crystallography of Al3Sc dendrites in as-casted Al-10at.%Sc and Al-20at.%Sc samples is examined using electron backscatter diffraction (EBSD). With increasing Sc content, the fraction of Al3Sc also increases. The Al3Sc dendrites exhibit a cubic relationship with the Al matrix in both alloys. However, in Al-10%Sc alloys, the facets of the Al3Sc dendrites are parallel to {001} planes, while twinning is observed in Al-20at.%. The twinning plane is parallel to the {111} plane, and the dendrite growth direction aligns with the directions. The different morphologies of the dendrite structures in these two alloys are discussed in relation to thermodynamic and kinetic considerations based on the phase diagram and nucleation rate.

Keywords

• Al-Sc alloy
• Al₃Sc
• twin
• dendrite
• crystallography