Nanostructured Fe,Co-Codoped MoO₃ Thin Films

Abstract

Molybdenum oxide (MoO3) and Fe,Co-codoped MoO3 thin films obtained by spray pyrolysis have been in-depth investigated to understand the effect of Co and Fe codoping on MoO3 thin films. The effect of Fe and Co on the structural, morphological and optical properties of MoO3 thin films have been studied using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and energy-dispersive X-ray analysis (EDAX), optical and photoluminescence (PL) spectroscopy, and electropyroelectric methods. The XRD patterns demonstrated the formation of orthorhombic α-MoO3 by spray pyrolysis. SEM characterization has shown an increase in roughness of MoO3 thin films by Fe and Co doping. Optical reflectance and transmittance measurements have shown an increase in optical band gap with the increase in Fe and Co contents. Thermal conductivity and thermal diffusivity of Fe,Co-doped MoO3 were 24.10⁻25.86 Wm−1K−1 and 3.80 × 10−6⁻5.15 × 10−6 m2s−1, respectively. MoO3 thin films have shown PL emission. Doping MoO3 with Fe and Co increases emission in the visible range due to an increase number of chemisorbed oxygen atoms. The photodegradation of an aqueous solution of methylene blue (MB) depended on the content of the codoping elements (Fe,Co). The results showed that a degradation efficiency of 90% was observed after 60 min for MoO3: Fe 2%-Co 1%, while the degradation efficiency was about 35% for the undoped MoO3 thin film.

Keywords

• spray pyrolysis
• thin films
• MoO₃
• X-ray diffraction
• morphology
• optical properties
• transmission electron microscopy (TEM)
• thermal
• photocatalysis