The significant impact of Nb on ferrite transformation, both in terms of solute drag effect (SDE) and interphase precipitation, was investigated quantitatively. Ferrite transformation kinetics were characterized using thermal expansion experiments and theoretical calculations. The microstructures were characterized using high−temperature confocal laser scanning microscopy (CLSM), a field−emission scanning electron microscope (FESEM), and a transmission electron microscope (TEM). Under a higher driving force, interphase precipitations were observed in the sample with a higher Nb content. A three−dimensional (3D) reconstruction method was used to convert the two−dimensional (2D) image of interphase precipitation into a three−dimensional model for a more typical view. The SDE and interphase precipitation had opposite effects on the kinetics of ferrite transformation. A lower Nb content showed a strong contribution to the SDE, which delayed ferrite transformation. A higher concentration of Nb was expected to enhance the SDE, but the inhibition effect was eliminated by the interphase precipitation of NbC during interfacial migration. Both the experimental results and theoretical calculations confirmed this phenomenon.