Butter layers of different thicknesses were successfully deposited on ferritic steel by using the tungsten arc welding (TIG) process. The effects of butter layer thickness on the microstructural characteristics, elemental distribution, and mechanical properties of underwater wet 16Mn/304L dissimilar welded joints were investigated. The results showed that the butter layer significantly changed the microstructure and elemental distribution of 16Mn/304L joints. As the thickness of butter increased, the heat-affected zone (HAZ) at the ferritic steel side changed from the original 16Mn steel to the ERNiCrMo-3 butter layer. The martensite content in HAZ also exhibited a downward trend. When the thickness of the butter layer exceeded 6 mm, the microstructure of HAZ at the ferritic steel side was composed of ferrite and pearlite, instead of quenched martensite. The microhardness of underwater dissimilar steel welded joints significantly reduced due to the absence of martensite. The addition of the butter layer increased the ultimate tensile strength from 515 MPa to 565 MPa. The results of this work could provide a robust basis for future applications of dissimilar steel structures.