Elaboration of wide bandgap CIGS on silicon by electrodeposition of stacked metal precursors and sulfur annealing for tandem solar cell applications

Abstract

A method was developed for the electrodeposition of Cu-In-Ga precursor layers to elaborate Cu(In,Ga)(S,Se)2 (CIGS) thin films on silicon substrates for future application as silicon/wide-gap CIGS tandem solar cells. An underlayer of Ag was first deposited on silicon substrates to ensure a good adhesion of the electrodeposited stack and to serve as cathode during the deposition process. Cu, In and Ga layers were then sequentially electrodeposited. Ag-Cu-In-Ga precursor layers were finally subjected to elemental sulfur annealing at 600 °C. Formation of compact and adherent AgCIGS is observed. X ray diffraction and photoluminescence analyses confirm the formation of wide-gap CIGS of about 1.6 eV, with a spontaneous gallium grading over the depth of the sample leading to the formation of a bi-layer structure with a gallium rich layer at the interface with silicon.

Keywords

• tandem solar cells
• pure sulfide cigs
• silicon
• electrodeposition
• silver-sulfide