How to achieve nanometer flat surfaces: Pulsed electrochemical machining of bulk metallic glass

Abstract

The Bulk Metallic Glass (BMG) Vitreloy 105 (Zr52.5Ti5Ni14.6Cu17.9Al10) as well as two crystalline reference materials of the same composition were machined with Pulsed Electrochemical Machining (PECM). One reference material was nano crystalline with an average grain size of 11 nm and the second one was a fine grain crystalline sample with an average grainsize of 110 nm. The goal was to achieve maximum surface quality in terms of roughness by utilizing a readily available industrial process. Samples were characterized by tactile profilometer, atomic force microscopy and electron microscopy methods. The results show superior surface quality of the amorphous samples over the reference materials with an average roughness depth as low as 1 nm. The observed dissolution mechanism of the BMG differs from the reference materials -as in contrast to the crystalline alloys that show a passive layer formation - no such surface layer other than the native oxide could be observed. The PECM procedure is found to be a promising post-processing step for BMGs with a resulting surface that can face even the most challenging surface quality requirements.

Keywords

• Bulk metallic glasses
• Pulsed electrochemical machining
• BMG post-processing
• Superior surface quality