The Dynamic Viscoelasticity of Dental Soft Polymer Material Containing Citrate Ester-Based Plasticizers

Abstract

The aim of this study was to investigate the dynamic viscoelasticity of dental soft polymer material containing citrate ester-based plasticizers. Three kinds of citrate ester-based plasticizer (Citroflex® C-2: TEC, Citroflex® A-2: ATEC, and Citroflex® A-4: ATBC), with the combination of 5 wt% ethyl alcohol, were used as the liquid phase. The dynamic viscoelastic properties of nine ethyl methacrylate polymers: (A, B, C, D, E, F, G, H, and I) were immersed in 37 °C distilled water for 0, 1, 3, 7, 14 and 30 days, respectively. The dynamic viscoelastic properties were measured at 37 °C with an automatic dynamic mechanical analyzer. The shear storage modulus (G′), shear loss modulus (G″), and loss tangent (tan δ) were determined at 1 Hz. These parameters were statistically analyzed by two-way and one-way ANOVA and Tukey’s multiple comparison test at a predetermined significance level of 0.05. A significant difference was found among the materials in terms of the dynamic viscoelasticity. The materials containing citrate ester-based plasticizer ATBC showed the most stable dynamic viscoelasticity. Considering the limitations of this study, the results suggest that the inclusion of citrate ester-based plasticizer can improve the durability of dental soft polymer materials.

Keywords

• dynamic viscoelasticity
• dental soft polymer
• citrate ester-based plasticizer
• tissue conditioner