Permeabilities and Mechanical Properties of Hardened Cement Pastes Modified with Sodium Laurate and Nano Silica

Abstract

In this work, a method of imparting hydrophobicity and high strength to hardened cement paste (HCP) is proposed. Sodium laurate (SL) was used as a hydrophobic modifier and nano silica (NS) as a pozzolan. The HCP was modified by SL and NS simultaneously. HCP modified with different contents of SL and NS was prepared. Surface wettability, micro-structures, chemical composition, and organic structure were systematically studied using contact angle (CA) measurement, scanning electron microscope (SEM) observation, X-ray photoelectron spectroscopy (XPS), and attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR), respectively. The surface CA of the sample is 138.5° and has high hydrophobicity. Compared with the reference sample, the water absorption of the modified sample reduced by 96.55%, while the compressive strength only reduced by 6.91%. Therefore, using hydrophobic modifier and reinforcing agent as cement admixture is an effective method to endow concrete with hydrophobicity and high strength at the same time.

Keywords

• hardened cement paste
• hydrophobicity
• nano silica
• sodium laurate
• compressive strength
• water absorption