Influence of Preheating Self-Adhesive Cements on the Degree of Conversion, Cell Migration, and Cell Viability

  • Henrique Cantarelli,
  • Fernando Antonio Costa Xavier,
  • Fernando Freitas Portella,
  • Keiichi Hosaka,
  • Eduardo Galia Reston,
  • Louis Hardan,
  • Rim Bourgi,
  • Celso Afonso Klein-Junior

DOI
https://doi.org/10.3390/applmech5030031
Journal volume & issue
Vol. 5, no. 3
pp. 553 – 562

Abstract

Read online

Enhancing the degree of polymerization can mitigate the cytotoxic effects of resinous materials, as residual monomers have been identified as a significant contributor to cytotoxicity. Hence, the aim of the current research was to evaluate the influence of preheating self-adhesive cements at 39 °C on cell migration, cytotoxicity, and degree of conversion. RelyX U200, Set PP, and MaxCem Elite were subjected to Fourier Transform Infrared Spectroscopy–Attenuated Total Reflection (FTIR–ATR). Self-adhesive resin cements were applied onto an ATR device, with samples subjected to either heated or room temperature conditions, followed by photoactivation. For the cytotoxicity analysis, extracts (24 h and 7 days) were placed in contact with NIH/3T3 cells. For cell migration, images were captured of each sample until the possible closure of the cleft occurred. A two-way analysis of variance (ANOVA) was conducted to assess the effect of preheating on the degree of conversion and cell viability within the self-adhesive cements tested. A significance level of 5% was set for statistical purposes. In the results of the degree of conversion, preheating did not improve the conversion of cements (p > 0.05). For the 3-(4-5-dimethyl-2-thiazolyl)-2,5-diphenyl-2H-tetrazolium bromide (MTT), preheating did not improve the results within 24 h, however, it generated positive results within 7 days for the Set PP resin cement (p < 0.05). For cell migration, high rates of cell death were found in all groups. It is concluded that preheating at 39 °C causes a positive effect only in increasing the cell viability of the Set PP resin cement and that both materials analyzed are highly cytotoxic.

Keywords