Pb1-xMnxTe single crystals and their structural properties

Abstract

Pb1-xMnxTe crystals were grown by the vertical Bridgman method. Their structural properties were observed both by optical microscopy after chemical polishing and ething, and by X-ray powder diffraction analysis. A solution of 5 vol. % Br2 in HBr at room temperatur, for an exposure of 2 min was determined for chemical polishing. Asolution of 20 g KOH in 1 ml H2O2, 2 ml glycerol (C3H8O3), and 20 ml H2O at room temperature for an exposure for 6 min was found to be a suitable etching solution. The obtained results are discussed and compared with published data.

Keywords

• lead manganese telluride
• bridgman method
• structural properties
• etching
• chemical polishing