Mechanical Properties of Dental Alloys According to Manufacturing Process

Abstract

The purpose of this study is to investigate the effect of the fabrication method of dental prosthesis on the mechanical properties. Casting was produced using the lost wax casting method, and milling was designed using a CAD/CAM program. The 3D printing method used the SLS technique to create a three-dimensional structure by sintering metal powder with a laser. When making the specimen, the specimen was oriented at 0, 30, 60, and 90 degrees. All test specimens complied with the requirements of the international standard ISO 22674 for dental alloys. Tensile strength was measured for yield strength, modulus of elasticity and elongation by applying a load until fracture of the specimen at a crosshead speed of 1.5 ± 0.5 mm/min (n = 6, modulus of elasticity n = 3). After the tensile test, the cross section of the fractured specimen was observed with a scanning electron microscope, and the statistics of the data were analyzed with a statistical program SPSS (IBM Corp. Released 2020. IBM SPSS Statistics for Windows, Version 27.0. Armonk, NY, USA: IBM Corp.) and using Anova and multiple comparison post-tests (scheffe method). The yield strength was the highest at 1042 MPa at an angle of 0 degrees in the specimen produced by 3D printing method, and the elongation was the highest at 14% at an angle of 90 degrees in the specimen produced by 3D printing method. The modulus of elasticity was the highest at 235 GPa in the milled specimen. In particular, the 3D printing group showed a difference in yield strength and elongation according to the build direction. The introduction of various advanced technologies and digital equipment is expected to bring high prospects for the growth of the dental market.

Keywords

• casting
• dental alloy
• dentistry
• mechanical properties
• milling
• 3D printing