Facile Synthesis of Dual-Network Polymer Hydrogels with Anti-Freezing, Highly Conductive, and Self-Healing Properties

Abstract

We report the synthesis of poly(acrylamide-co-acrylic acid)/sodium carboxy methyl cellulose (PAMAA/CMC-Na) hydrogels, and subsequent fabrication of dual-network polymer hydrogels (PAMAA/CMC-Na/Fe) using as-prepared via the salt solution (FeCl3) immersion method. The created dual-network polymer hydrogels exhibit anti-swelling properties, frost resistance, high conductivity, and good mechanical performance. The hydrogel swells sightly when immersed in solution (pH = 2~11). With the increase in nAA:nAM, the modulus of elasticity experiences a rise from 1.1 to 1.6 MPa, while the toughness undergoes an increase from 0.18 to 0.24 MJ/m3. Furthermore, the presence of a high concentration of CMC-Na also contributes to the enhancement of mechanical strength in the resulting hydrogels, ascribing to enhanced physical network of the hydrogels. The minimum freezing point reaches −21.8 °C when the CMC-Na concentration is 2.5%, owing to the dissipated hydrogen bonds by the coordination of Fe3+ with carboxyl (-COO−) in CMC-Na and PAMAA. It is found that the conductivity of the PAMAA/CMC-Na/Fe hydrogels gradually decreased from 2.62 to 0.6 S/m as the concentration of CMC-Na rises. The obtained results indicates that the dual-network hydrogels with high mechanical properties, anti-swelling properties, frost resistance, and electrical conductivity can be a competitive substance used in the production of bendable sensors and biosensors.

Keywords

• dual-network hydrogels
• swelling resistance
• frost resistance
• conductivity
• self-healing