Starch consolidation of SiC ceramics: processing and low-temperature sintering in an air atmosphere

Abstract

Highly porous SiC ceramics containing borax decahydrate were produced by a starch consolidation method in which corn starch was used as a shaping and pore-forming additive. Four different compositions were prepared with different SiC:borax decahydrate ratios and corn starch content. Mixtures with a solid ratio of 55 wt.% were cast in non-porous molds and heated at 80°C for shaping. The starch consolidation technique enabled the shaping of SiC ceramics with different forms and sizes. Simultaneous thermogravimetry and differential thermal analysis of the SiC-borax decahydrate mixture showed that melting took place at below 600°C, as a result of which sintering was carried out at the relatively low temperature, of 600°C in the air using borax decahydrate as a sintering additive. Phase analysis showed that oxidation of SiC did not take place, since no cristobalite phase was detected. Density measurement and mercury porosimetry studies showed that highly porous (70–89% porosity) SiC ceramics with pore size values ranging from 14 to 18 μm were produced. SEM microstructures of each composition revealed that a strong neck had been formed between the SiC particles in spite of the low sintering temperature.

Keywords

• starch consolidation
• porous sic
• tg–dta
• sintering under atmospheric conditions
• low–temperature sintering