Investigation of AgI-Based Solid Solutions with Ag₂CO₃

Abstract

The formation phenomena of silver carbonate (Ag2CO3)–silver iodide (AgI) solid solutions were investigated by X-ray diffraction, thermogravimetry-differential thermal analysis, and electrical conductivity measurement. Results revealed that AgI and Ag2CO3 reacted with each other when mixed at room temperature. The reaction products were classified into three types: (1) AgI-based solid solutions in the AgI-rich region for x = 10% or less in x Ag2CO3–(1 − x) AgI; (2) Ag2CO3-based solid solutions in the Ag2CO3-rich region for x = 60% or more; and (3) silver carbonate iodides in the intermediate range for x between 10% and 60%. For the AgI-based solid solutions, the incorporation of Ag2CO3 into the AgI lattice expanded the unit cell and enhanced electrical conductivity. The solubility limit of Ag2CO3 into the AgI lattice estimated from the differential thermal analysis was x ≈ 5%.

Keywords

• solid electrolyte
• ionic conductor
• solid solution
• silver carbonate iodide
• AgI
• Ag₂CO₃