VISCOSE BASED MAGNETIC YARNS – PHYSICAL AND MECHANICAL CHARACTERIZATION

Abstract

In the context of the rapid growth in the number of electrical and electronic devices and accessories that emit electromagnetic energy in different frequency bands we present and characterize here several magnetic functionalized viscose twisted yarns. A 100% viscose twisted staple yarn was covered through an in-house developed process with a polymeric solution containing micrometric sized barium hexaferrite magnetic powder. The in-house developed process allows deposition of micrometric thickness polymeric paste layer on the yarn surface. Barium hexaferrite is a hard magnetic material exhibiting high chemical stability and corrosion resistivity, relatively large saturation and residual magnetization and microwave absorbing properties. Five different percentages of the magnetic powder in the polymer solution were used, i.e. ranging from 15 wt% to 45 wt%. Physical characterization shows a very good adherence between the highly hygroscopic viscose staple fibers and the polymeric solution that contains polyvinyl acetate and polyurethane as binders. SEM images evidenced the fact that the polymeric solution penetrated more than 1/3 of the yarn diameter. The concentration of magnetic powder in the polymeric solution has a direct influence on the coating amount, diameter and density. The mechanical characterization of the coated yarns revealed that the breaking force is increasing with increasing magnetic powder content up to o certain value and then decreased because the magnetic layer became stiffer. At the same time, the elongation at brake is decreasing.

Keywords

• viscoze coated yarn
• magnetic particles
• polymeric coating solutions
• adherence
• mechanicalproperties