The Microstructure and Mechanical Properties of Poplar Catkin Fibers Evaluated by Atomic Force Microscope (AFM) and Nanoindentation

Abstract

In this study, the microstructure and mechanical properties of poplar (Populus tomentosa) catkin fibers (PCFs) were investigated using field emission scanning electron microscope, atomic force microscopy (AFM), X-ray diffraction, and nanoindentation methods. Experimental results indicated that PCFs had a thin-wall cell structure with a large cell lumen and the hollow part of the cell wall took up 80 percent of the whole cell wall. The average diameters of the fiber and cell lumen, and the cell wall thickness were 5.2, 4.2, and 0.5 µm, respectively. The crystallinity of fibers was 32%. The AFM images showed that the orientation of microfibrils in cell walls was irregular and their average diameters were almost between 20.6−20.8 nm after being treated with 2 and 5 wt.% potassium hydroxide (KOH), respectively. According to the test of nanoindentation, the average longitudinal-reduced elastic modulus of the PCF S2 layer was 5.28 GPa and the hardness was 0.25 GPa.

Keywords

• poplar catkin fiber
• microstructure
• cellulose nano-fibrils