Effect of Phenol Formaldehyde Resin Penetration on the Quasi-Static and Dynamic Mechanics of Wood Cell Walls Using Nanoindentation

Abstract

To evaluate the effects of phenol formaldehyde (PF) resin modification on wood cell walls, Masson pine (Pinus massoniana Lamb.) wood was impregnated with PF resin at the concentrations of 15%, 20%, 25%, and 30%, respectively. The penetration degree of PF resin into wood tracheids was quantitatively determined using confocal laser scanning microscopy (CLSM). The micromechanical properties of the control and PF-modified wood cell walls were then analyzed by the method of quasi-static nanoindentation and dynamic modulus mapping techniques. Results indicated that PF resin with low molecular weight can penetrate deeply into the wood tissues and even into the cell walls. However, the penetration degree decreased accompanying with the increase of penetration depth in wood. Both the quasi-static and dynamic mechanics of wood cell walls increased significantly after modification by the PF resin at the concentration less than 20%. The cell-wall mechanics maintained stable and even decreased as the resin concentration was increased above 20%, resulting from the increasing bulking effects such as the decreased crystallinity degree of cellulose. Furthermore, the mechanics of cell walls in the inner layer was lower than that in the outer layer of PF-modified wood.

Keywords

• phenol formaldehyde resin
• wood modification
• cell-wall mechanics
• nanoindentation
• modulus mapping