Omega Phase Formation in Ti–3wt.%Nb Alloy Induced by High-Pressure Torsion

Abstract

It is well known that severe plastic deformation not only leads to strong grain refinement and material strengthening but also can drive phase transformations. A study of the fundamentals of α → ω phase transformations induced by high-pressure torsion (HPT) in Ti–Nb-based alloys is presented in the current work. Before HPT, a Ti–3wt.%Nb alloy was annealed at two different temperatures in order to obtain the α-phase state with different amounts of niobium. X-ray diffraction analysis, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were applied for the characterisation of phase transitions and evolution of the microstructure. A small amount of the β-phase was found in the initial states, which completely transformed into the ω-phase during the HPT process. During HPT, strong grain refinement in the α-phase took place, as did partial transformation of the α- into the ω-phase. Therefore, two kinds of ω-phase, each with different chemical composition, were obtained after HPT. The first one was formed from the β-phase, enriched in Nb, and the second one from the α-phase. It was also found that the transformation of the α-phase into the ω-phase depended on the Nb concentration in the α-Ti phase. The less Nb there was in the α-phase, the more of the α-phase was transformed into the ω-phase.

Keywords

• high-pressure torsion
• in situ high-temperature X-ray diffraction
• Ti alloys
• phase transformations
• scanning electron microscopy
• transmission electron microscopy