Interfacial Reactions between Mg-40Al and Mg-30Y Master Alloys

Abstract

Interfacial reactions between Mg-40Al and Mg-30Y master alloys were investigated at intervals of 25 °C in the 350–400 °C by using a diffusion couple method. Noticeable reaction layers were formed at the interfaces of the diffusion couples. The concentration profiles of the reaction layers were characterized. The diffusion path of the diffusion couple at 400 °C is constructed on the Mg-Al-Y ternary isothermal temperature phase diagram. The phases of the reaction layer were characterized by X-ray diffraction. The interfacial reaction thermodynamics of diffusion couples were studied. These results indicate that Al2Y is the only new formed intermetallic phase in the reaction layers. The growth constants of the reaction layers were calculated. In the reaction layer II, the integrated interdiffusion coefficients of Al are higher than Y, the diffusion activation energy of Y is higher than that of Al.

Keywords

• magnesium alloys
• interface reaction
• diffusion
• intermetallic phases