In this study, the decomposition of a martensite/austenite (M/A) microconstituent in bainitic steels was analyzed using differential scanning calorimetry (DSC) data in conjunction with Kissinger’s and Johnson–Mehl–Avrami–Kolmogorov (JMAK)’s formulas. In bainitic steel subjected to austempering heat treatment, the presence of an M/A microstructure adversely affects the mechanical properties. According to the kinetic equations derived, it is observed that after tempering the sample at 600 °C for 4000 s, the generation of each phase reaches its maximum. The SEM images taken before and after tempering reveal extensive decomposition of the M/A constituent in the microstructure. The proportion of the M/A microstructure decreased significantly from about 10% before tempering to less than 1% after. Additionally, the content of residual austenite also reduced nearly to zero. These observations are consistent with the predictions of the kinetic equations.