Mechanical Properties of Parallel TDG Bamboo Laminated Columns with Tough and Grove Joints
Abstract
The problem of bamboo’s strength depends on the length used. From past experiments, it was found that the physical properties of bamboo have thickness at the bottom and a tapered end, resulting in the strength of the bamboo in each part being different. The bottom part can resist more compression than the tip, which corresponds to the physical characteristics of bamboo. To use bamboo for main construction, such as columns, many select raw bamboo that measures approximately 3 m from the ground and is considered the strongest part. The present bamboo laminated products are limited to 2.4 m in length due to the capabilities of today’s compression machines and the factor of length as mentioned above. The column is an important infrastructure, which must have sufficient strength and capacity to solve the problem of high space. However, based on the above limitations, it is particularly important to study the connectivity of increasing column length. A wood joint is a traditional method to secure two pieces of wood together. Tongue and groove joints are most common in floorings, such as wood flooring, laminate flooring, and flooring. One of the hardest methods of securing wood is end to end of edge to edge. In order to further develop green building materials, TDG bamboo is processed into laminated columns (TDGLC). It is considered important because, in addition to increasing income for farmers, it will also enable the development of building materials to replace wood in the future. Therefore, this research demonstrates the benefits of developing locally available materials such as bamboo. To develop laminated bamboo columns for use in a structure, we chose 3–4-year-old TDG bamboo and glued it to obtain a 100 mm cross-section column in order to maximize the benefits of using TDG bamboo for real use. Test specimens are joined by tongue-groove joints to a column length of 1 m, 2 m, and 3 m by joining joints in four different areas: Top (T), middle (M), top-bottom (TB), and bottom (B), to test for compressive strength. The test results showed that TDGLC + TG at the top specimens 4L01 T–4L03 T can resist a load range of 100–65%, and for the middle specimen 4L01 M–4L03 M, the load is between 88 and 57%. At the top-bottom 4L01 TB–4L03 TB, the load is between 30 and 20%. At the bottom 4L01 B–4L03 B, the load is between 28 and 18%.
Keywords