Boletín de la Sociedad Española de Cerámica y Vidrio (Oct 2005)
Medida de la dureza de sólidos mediante nanoindentación
Abstract
Hardness is not readily measurable by means of instrumented indentation since the value of the contact area depends on the pile-up or sink-in occurring near the contact surface of the sample. The most widespread method to estimate it by means of the loading/unloading curve of indentation, Oliver and Pharr’s method, deviates, in the extreme cases, up to a 25% from the real values since it only takes into account the elastic deflection. In this work, a new correction based on Oliver and Pharr’s method is proposed that agrees with the numerical calculations. Plastic hardening behaviour of the sample must be known to accurately estimate the contact area.<br><br>La medida de la dureza mediante indentación con registro de carga y desplazamiento no es evidente, dada la incertidumbre sobre el tamaño de huella debido al levantamiento (pile-up) o hundimiento (sink-in) plásticos de la superficie de la muestra alrededor del indentador. El método más utilizado para la medida de la dureza mediante la curva de carga/descarga de indentación, el de Oliver y Pharr, sólo tiene en cuenta hundimiento elástico, por lo que el error en la medida de la dureza y el módulo de Young puede llegar hasta un 25% en los casos más extremos. En el presente trabajo se discute una posible corrección al método de Oliver y Pharr para una obtención más ajustada del área de contacto de la huella. Esta corrección requiere de un conocimiento a priori o a posteriori del comportamiento plástico del material.