Effect of As-Built and Ground Surfaces on the Fatigue Properties of AlSi10Mg Alloy Produced by Additive Manufacturing

Abstract

The present work concerns the influence of surface (machined, as-built) on the fatigue resistance of AlSi10Mg produced by a powder-bed laser process. The competition between defects and surface roughness is assessed by using Kitagawa-type diagrams. Samples are printed along three directions: 0°, 45° and 90°. After axial fatigue tests with a load ratio of R = −1, all the fracture surfaces are carefully analysed. The initiation sites can be (i) a defect, (ii) the surface roughness, (iii) the surface ripple. The results indicate that ground surfaces lead to the same fatigue life as as-built surfaces. It is also shown that T6 treatment improves the fatigue resistance. However, when specimen surfaces are as-built or ground, it is difficult to correlate the fatigue results with ‘isolated defect size analysis’ neither roughness parameter for an as-built surface. Therefore, microstructure, residual stresses or multiple initiation should be further analysed to understand the results.

Keywords

• fatigue
• defect
• as-built surface