Magnetic Metallic Nanoparticles Coated with Carbon for the Catalytic Removal of Bromate from Water

Abstract

Bromate, often detected in drinking water, is associated with a significant risk of cancer. Catalytic reduction has been recognized as an effective treatment technique to remove ions by reducing them over metal catalysts in the presence of a reducing agent, usually hydrogen. This work aims to synthesize metallic magnetic nanoparticles of iron oxide (FeO) and mixed iron oxides with manganese (MnFeO), cobalt (CoFeO), and copper (CuFeO) coated with carbon via chemical vapor deposition (C-MNP) to be applied as catalysts to the reduction of bromate in water. The use of magnetic nanoparticles coated with carbon enables catalyst recovery via magnetic separation and takes advantage of the catalytic properties of the carbon materials. The iron particles proved to be the most promising catalysts for the reduction of bromate into bromide, the highest removal being obtained with the CFeO@CVD750 sample, resulting in a 99% conversion after 120 min of reaction under the conditions tested. Due to its magnetic nature, the catalytic material was easily removed after the reaction and applied in four consecutive cycles without losing its catalytic properties. These results highlight the great potential of carbon-coated magnetic nanoparticles for reducing bromate in water.

Keywords

• metallic magnetic materials
• chemical vapor deposition
• bromate reduction
• carbon