Metals (Oct 2021)
Pressure-Assisted Development and Characterization of Al-Fe Interface for Bimetallic Composite Castings: An Experimental and Statistical Investigation for a Low-Pressure Regime
Abstract
A review of the available literature indicates that the development of metal-reinforced castings present intriguing prospects but carry inherent challenges owing to differences in thermal coefficients, chemical affinities, diffusion issues and the varying nature of intermetallic compounds. It is supported that pressure application during solidification may favorably influence the dynamics of the aforementioned issues; nevertheless, not only certain limitations have been cited, but also some pressure and process regimes have not yet been investigated and optimized. This work employs the pressure-assisted approach for bimetallic steel-reinforced aluminum composite castings at a low-pressure regime and thoroughly investigates the role of three process parameters, namely pouring temperature (800–900 °C), pressure (10–20 bars) and holding time (10–20 s), for producing sound interfaces. The Taguchi L9 orthogonal array has been employed as the Design of the Experiment, while dominant factors have been determined via analysis of variance and the grey relational analysis multi-objective optimization technique. Supplementary analysis through optical micrographs, scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) has been utilized to quantify interfacial layer thicknesses and to study microstructural and compositional aspects of the interface. Nano-indentation tests under static and dynamic loading have also been performed for mechanical strength characterization. It has been found that uniform interfaces with verifiable diffusion are obtainable, with the pouring temperature being the most influential parameter (percentage contribution 92.84%) in this pressure regime. The experiments performed at optimum conditions of pouring temperature, applied pressure and holding time produced a ~328% thicker interface layer, 19.42% better nano-hardness and a 19.10% improved cooling rate as compared to the minimum input values of the said parameters.
Keywords