Study on synthesis of carboxymethyl cellulose from pineapple leaf waste and its potential applications as a thickener

Abstract

In this study, cellulose and hemicellulose were successfully extracted from pineapple leaf waste at yields of 58.8 and 16.1% by dried weight, respectively. Carboxymethyl cellulose (CMC) was synthesised from pineapple leaf cellulose by an esterification process using sodium hydroxide (NaOH) and monochloroacetic acid (MCA) with isopropanol as the supporting medium. Preparation of CMC was investigated by varying three free factors, namely, NaOH concentration, MCA dose, and cellulose size. The carboxymethylation process was optimised to produce CMC with differing degrees of substitution (DS). The highest DS of CMC (0.86) was obtained with 15% (w/v) NaOH solution, 0.6 g of MCA/g cellulose, and 50 μm cellulose. The obtained CMC were characterised by FTIR spectroscopy, SEM images and XRD diffractions. Moreover, the thickening performance of obtained CMC was also determined. The influence of the CMC’s molecular weight and degree of substitution on the viscosity of 1% (w/v) aqueous solution was tested. The experimental results suggest that the viscosity of the solution increases with increasing molecular weight and degree of substitution of CMC.

Keywords

• carboxymethyl cellulose
• cellulose viscosity
• hemicellulose
• pineapple leaf waste