Role of Mg Impurity in the Water Adsorption over Low-Index Surfaces of Calcium Silicates: A DFT-D Study

Abstract

Calcium silicates are the most predominant phases in ordinary Portland cement, inside which magnesium is one of the momentous impurities. In this work, using the first-principles density functional theory (DFT), the impurity formation energy (Efor) of Mg substituting Ca was calculated. The adsorption energy (Ead) and configuration of the single water molecule over Mg-doped β-dicalcium silicate (β-C2S) and M3-tricalcium silicate (M3-C3S) surfaces were investigated. The obtained Mg-doped results were compared with the pristine results to reveal the impact of Mg doping. The results show that the Efor was positive for all but one of the calcium silicates surfaces (ranged from −0.02 eV to 1.58 eV), indicating the Mg substituting for Ca was not energetically favorable. The Ead of a water molecule on Mg-doped β-C2S surfaces ranged from –0.598 eV to −1.249 eV with the molecular adsorption being the energetically favorable form. In contrast, the Ead on M3-C3S surfaces ranged from −0.699 eV to −4.008 eV and the more energetically favorable adsorption on M3-C3S surfaces was dissociative adsorption. The influence of Mg doping was important since it affected the reactivity of surface Ca/Mg sites, the Ead of the single water adsorption, as well as the adsorption configuration compared with the water adsorption on pristine surfaces.

Keywords

• calcium silicates
• first-principles DFT
• Mg doping
• water adsorption
• structural and electronic properties