Cast High-Manganese Steel – the Effect of Microstructure on Abrasive Wear Behaviour in Miller Test

Abstract

The results of the modification of austenitic matrix in cast high-manganese steel containing 11÷19% Mn with additions of Cr, Ni and Ti were discussed. The introduction of carbide-forming alloying elements to this cast steel leads to the formation in matrix of stable complex carbide phases, which effectively increase the abrasive wear resistance in a mixture of SiC and water. The starting material used in tests was a cast Hadfield steel containing 11% Mn and 1.34% C. The results presented in the article show significant improvement in abrasive wear resistance and hardness owing to the structure modification with additions of Cr and Ti.

Keywords

• Austenite high manganese steels
• Microstructure
• Abrasive wear resistance
• Miller slurry machine test