Polymers (Apr 2024)
Enhancing the Weld Quality of Polylactic Acid Biomedical Materials Using Rotary Friction Welding
Abstract
Polylactic acid (PLA) stands out as a biomaterial with immense potential, primarily owing to its innate biodegradability. Conventional methods for manufacturing PLA encompass injection molding or additive manufacturing (AM). Yet, the fabrication of sizable medical devices often necessitates fragmenting them into multiple components for printing, subsequently requiring reassembly to accommodate the constraints posed by the dimensions of the AM platform. Typically, laboratories resort to employing nuts and bolts for the assembly of printed components into expansive medical devices. Nonetheless, this conventional approach of jointing is susceptible to the inherent risk of bolts and nuts loosening or dislodging amid the reciprocating movements inherent to sizable medical apparatus. Hence, investigation into the joining techniques for integrating printed components into expansive medical devices has emerged as a critical focal point within the realm of research. The main objective is to enhance the joint strength of PLA polymer rods using rotary friction welding (RFW). The mean bending strength of welded components, fabricated under seven distinct rotational speeds, surpasses that of the underlying PLA substrate material. The average bending strength improvement rate of welding parts fabricated by RFW with three-stage transformation to 4000 rpm is about 41.94% compared with the average bending strength of PLA base material. The average surface hardness of the weld interface is about 1.25 to 3.80% higher than the average surface hardness of the PLA base material. The average surface hardness of the weld interface performed by RFW with variable rotational speed is higher than the average surface hardness of the weld interface performed at a fixed rotating friction speed. The temperature rise rate and maximum temperature recorded during RFW in the X-axis of the CNC turning machine at the outer edge of the welding part surpassed those observed in the internal temperature of the welding part. Remarkably, the proposed method in this study complies with the Sustainable Development Goals due to its high energy efficiency and low environmental pollution.
Keywords