Preparation Technique and Properties of Nano-TiO₂ Photocatalytic Coatings for Asphalt Pavement

Abstract

According to the characteristics of asphalt pavement, a kind of nano-TiO2 photocatalytic coating was prepared by using the emulsified asphalt as the carrier. All of its properties met the technical requirements. An exhaust gas degradation test device and its test steps were developed. The evaluation indexes, cumulative degradation rate, and degradation efficiency, were put forward. From the two aspects of the nano-TiO2 content in photocatalytic coatings and the spraying amount of photocatalytic coatings in the surface of slabs (300 mm × 300 mm), the exhaust gas degradation effects, the performances of skid resistance, and the water permeability of asphalt mixture were analyzed. The test results showed that the cumulative degradation rate of exhaust gas was better when nano-TiO2 content was increased in the range of 0⁻8% and the spraying amount was changed in the range of 0⁻333.3 g/m2. In practical engineering applications, the anti-skid performance of asphalt pavement can be satisfied when the spraying amount of photocatalytic coating was limited to under 550 g/m2. The spraying amount of nano-TiO2 photocatalytic coating had little effect on the water permeability of the asphalt mixture. Therefore, 8% nano-TiO2 content in the coating and a 400 g/m2 spraying amount were finally recommended based on the photocatalytic properties, as well as for economic reasons.

Keywords

• preparation technique
• emulsified asphalt
• nano-TiO₂
• photocatalytic coating
• degradation of exhaust gas