Metallographic Study and Repeatability Analysis of γ' Phase Precipitates in Cored, Thin-Walled Castings Made from IN713C Superalloy

Abstract

The study describes the influence of a surface modification in cored, thin-walled castings of blades from IN-713C nickel superalloy on γ' phase precipitates. The blades were produced by using the investment casting process in the laboratory conditions as parts for a low-pressure turbine rotor. The microstructural observations of the γ' phase precipitates on the cross sections of the blades were performed. The observations were followed by quantitative metallography evaluation, and finally, a comparison of the precipitates between one blade with the conventionally applied ceramic core and one with the core covered layer contained a surface modifier (5% of CoAl2O4) was made.

Keywords

• IN 713C
• superalloy
• γ' phase
• metallography
• statistical analysis