Expansion volume of alkali activated foamed cork composites from tungsten mining mud waste with aluminium

Abstract

Several mixes of alkali activated foams from tungsten mud waste (MW), grounded glass (GG) and metakaolin (MK) were developed incorporating expanded granulated cork (EGC). This study presents preliminary results of the expansion process obtained with the addition of aluminium (AL) powder as a foaming agent. 0.3 wt.%, 0.4 wt.% to 0.5wt.% of AL powder were added to the alkali activated matrix. The physical and mechanical properties of the obtained foams, the effects of the type and amount of the foaming agent added are presented and discussed. Highly porous structures were obtained, with overall expansion up to 68.2% when the AL powder was added. The size and distribution of pores are shown. The compressive strength of foams in the case of highly porous structures achieved of 1.2 MPa for the samples containing 0.5 wt.% of AL powder. Mechanical and thermal properties of the cured structure are good and can therefore be used for applications in acoustic panels and lightweight prefabricated components for thermal insulation purposes.