Tm3+/Ho3+ profiled co-doped core area optical fiber for emission in the range of 1.6–2.1 µm

Abstract

Abstract Double-clad optical fiber with a multi-ring core profile doped with thulium and holmium fabricated by Modified Chemical Vapor Deposition Chelate Doping Technology (MCVD-CDT) is presented. The measured Tm2O3 and Ho2O3 complexes’ weight concentrations were 0.5% and 0.2% respectively. Numerical analyses show weakly guiding conditions and 42.2 µm of MFD LP01 at 2000 nm. The low NA numerical aperture (NA = 0.054) was obtained for the 20/250 µm core/cladding ratio optical fiber construction. The emission spectra in the range of 1.6–2.1 µm vs. the fiber length are presented. The full width at half maximum (FWHM) decreases from 318 to 270 nm for fiber lengths from 2 to 10 m. The presented fiber design is of interest for the development of new construction of optical fibers operating in the eye-safe spectral range.